Luger paint color
Hi there!!
Just wondering what color paint was used on the WW2 basic Luger (don't know the real name, new to this and all). Was it just black or more of a dark grey? Please let me know the exact color it was! If this sort of topic is here please let me know. Thanks |
04-22-2012, 07:46 AM | #2 |
User
Join Date: Mar 2008
Location: Marco Island, Florida
Posts: 4,867
Thanks: 1,685
Thanked 1,916 Times in 1,192 Posts
|
Welcome to the forum.
Lugers were never painted. The WW2 pistols were salt blued, which gave a very deep Blue/Black and sometimes a deep plum color on certain parts. Some post WW2 Lugers received "Parkerizing", which gives them a grey-green color, like our 1911's, M1 Carbines and Garand rifle's finishes. The original German manufacturers, however, never applied this type of finish. |
04-22-2012, 09:27 AM | #3 |
New User
Join Date: Apr 2012
Posts: 2
Thanks: 0
Thanked 0 Times in 0 Posts
|
Ugh, first post and a dumb question!
Well I figured since most guns are painted they would be. |
04-22-2012, 09:40 AM | #4 |
Super Moderator
Eternal Lifer LugerForum Patron Join Date: Jun 2002
Location: North of Spokane, WA
Posts: 15,909
Thanks: 1,986
Thanked 4,500 Times in 2,076 Posts
|
There were 'some' guns painted, but the vast majority have and were blued or browned, now newer guns, such as glocks and such, i don't know what their coating is?
Welcome and be sure to check out the stickies on the New Collectors area and the FAQ, it contains a lot of information; this is not to discourage you from posting. Ed
__________________
Edward Tinker ************ Co-Author of Police Lugers - Co-Author of Simson Lugers Author of Veteran Bring Backs Vol I, Vol II, Vol III and Vol IV |
04-22-2012, 10:20 AM | #5 | |
Lifer
Lifetime Forum Patron Join Date: Feb 2009
Location: ...on the 'ol Erie Canal...
Posts: 8,181
Thanks: 1,398
Thanked 4,438 Times in 2,327 Posts
|
Quote:
I do AR-15 barrels with ShooterSolutions 'manganese' solution, which gives a very-dark-gray to black color... I believe I've seen pics here of Lugers (Portuguese contract?) that had original Parkerized finish...
__________________
I like my coffee the way I like my women... ...Cold and bitter... |
|
04-22-2012, 10:52 AM | #6 | |
User
Join Date: Mar 2012
Posts: 61
Thanks: 8
Thanked 18 Times in 13 Posts
|
Quote:
Para USA and a few others use an IonBond process which electrically bonds coating with surface metal. Good old fashioned hot salt blueing is not very common anymore with manufacturers due to the labor and time it takes to do it properly, but as an old school collector, I just cannot get fired up to the new finishes. Duracoat?? Don't get me started....
__________________
Invest in precious metals: Lead, Brass and Primers |
|
The following 3 members says Thank You to tx_oil for your post: |
04-22-2012, 11:26 AM | #7 |
Moderator
Lifetime Forum Patron Join Date: Jun 2002
Location: Arizona/Colorado
Posts: 7,760
Thanks: 4,848
Thanked 3,099 Times in 1,426 Posts
|
I remember reading in Anthony van der Linden's book on FN pistols..it was either the French or Belgians were the first to paint pistols for their Navy handguns. Provided a more durable finish for salt water use.
__________________
Jerry Burney 11491 S. Guadalupe Drive Yuma AZ 85367-6182 lugerholsterrepair@earthlink.net 928 342-7583 (CO & AZ) Year Round 719 207-3331 (cell) "For those who Fight For It, Life has a flavor the protected will never know." |
04-22-2012, 12:08 PM | #8 |
Twice a Lifer
Lifetime Forum Patron Join Date: Mar 2011
Location: Atop the highest hill in Schuyler County NY
Posts: 3,282
Thanks: 7,007
Thanked 2,476 Times in 1,319 Posts
|
Does anyone know specifically what kind of finish was typically applied to Erma's diecast pistols, and how best to strip it off?
DP |
04-22-2012, 12:16 PM | #9 |
Moderator
Lifetime Forum Patron Join Date: Jun 2002
Location: Arizona/Colorado
Posts: 7,760
Thanks: 4,848
Thanked 3,099 Times in 1,426 Posts
|
David, The finish on those pistols always reminded me of the powder coating method...or perhaps an epoxy enamel?
__________________
Jerry Burney 11491 S. Guadalupe Drive Yuma AZ 85367-6182 lugerholsterrepair@earthlink.net 928 342-7583 (CO & AZ) Year Round 719 207-3331 (cell) "For those who Fight For It, Life has a flavor the protected will never know." |
The following 2 members says Thank You to lugerholsterrepair for your post: |
04-28-2012, 09:41 AM | #10 |
Twice a Lifer
Lifetime Forum Patron Join Date: Mar 2011
Location: Atop the highest hill in Schuyler County NY
Posts: 3,282
Thanks: 7,007
Thanked 2,476 Times in 1,319 Posts
|
Either of those might be a real bear to remove. A resilient finish of course would resist bead blasting, which I would prefer not to do, anyway. I've heard of some sort of "teflon" finish, but suspect that such was not used during the 60's. Powdercoating would by my current choice to replace the finish, as one series provides a thin-as-possible finish which is the most durable abailable; and its gloss can be adjusted to whatever I'd like.
I'm seeking a chemical approach as optimal, which would leave the original markings and surface texture completely alone. I may have to resort to careful sanding, but this may not adequately address the finish left in the markings. I'm hoping MEK, or similar, works. |
04-28-2012, 02:53 PM | #11 |
User
Join Date: Jun 2002
Location: Rio Rancho, New Mexico
Posts: 4,583
Thanks: 958
Thanked 970 Times in 276 Posts
|
I dont remember how I got the finish off, but I bet it was by bead blasting, I used a Brownells bake on spray finish. Not bad. This was circa 2003 so I dont remember all the particulars.
__________________
Thor's Luger Clinic http://members.rennlist.com/lugerman/ Ted Green (Thor Yaller Boots) 725 Western Hills Dr SE, Rio Rancho, NM 87124 915-526-8925 Email thor340@aol.com ----------------------------------- John3:3 Jesus answered and said to him, "Most assuredly, I say to you, unless one is born again, he cannot see the kingdom of God." |
The following member says Thank You to Thor for your post: |
04-30-2012, 11:08 PM | #12 |
Twice a Lifer
Lifetime Forum Patron Join Date: Mar 2011
Location: Atop the highest hill in Schuyler County NY
Posts: 3,282
Thanks: 7,007
Thanked 2,476 Times in 1,319 Posts
|
Robert,
I'm pretty sure we can rule out ferric nitrocarburizing because it only works with ferrous metals, let alone that it's application temps would make me worry about fusing the work in the process. The IonBond process sounds like the ticket, potentially. I'm thinking definitely not baked, everybody. Here's why: Last night I immersed a broken Erma La.22 toggle in MEK based stripper overnight. I baked another at 450 deg. Neither action had any affect on finish or structure of the test pcs. I used a brass brush to check for any motion of this finish and it was still hard and tight. One pass of a steel edged scraper yields bare metal. Jerry, I see what you're saying about the painted/coated look of the Ermas. I noticed that on the underside of the toggle scraps, it looked like such a coating might be there, but the topside of the part is smooth and glossy, likely buffed before finishing, and it has the same look as a blued finish on a steel gun. I think the "painted" look on the underside is a result of the surface texture of that part of the piece, preserved straight from the mold. I'd also consider electroplating, like black chrome. My former Ithaca/SKB shotgun's barrel was finished that way, with white chrome inside. And there was an Ithaca/Erma connection in the '70's. I'm hoping this thread lasts long enough to obtain a definitive answer. Apologies for highjacking the thread. The original topic sparked my initial question. Ted, when I view photo #2 full size, I can see the texture left by the bead blasting, particularly on the bbl. Slick work, there, by the way. You've changed a pistol that just got home from a long, hard day to one that's has a s__t, shower and shave and is now sporting a dinner tux. DP |
05-01-2012, 09:12 AM | #13 |
User
Join Date: Feb 2010
Location: Tennessee
Posts: 1,149
Thanks: 159
Thanked 663 Times in 318 Posts
|
I tried different chemicals when I restored my LA-22, but the only ones that would touch the finish also etched the metal. I got the impression that it's not a paint, but some form of chemical bluing. One thing that kind of works for finishing the pot metal is Birchwood Casey's "Aluminum Black". Some people obviously use this for refinishing display replicas made of similar metal, but it's very difficult to get a uniform finish and it also stinks real bad. You might be able to get decent results if you have enough patience with it, but I finally had to resort to blasting with fine aluminum oxide, then spraying with Brownell's bake on paint.
Still, the "semi-success" with Aluminum Black leads me to believe that there could actually be some form of "bluing" that can be used on this type of metal. One tip would be to search the model gun forums, seems like these guys struggle with the same problem and they may have a solution. |
05-01-2012, 09:19 AM | #14 |
User
Join Date: Mar 2008
Location: Marco Island, Florida
Posts: 4,867
Thanks: 1,685
Thanked 1,916 Times in 1,192 Posts
|
Would anodizing be a possibility? The aluminum frames on some of these inexpensive .22s look like anodizing.
|
The following member says Thank You to alanint for your post: |
05-01-2012, 12:38 PM | #15 |
User
Join Date: Jun 2002
Location: Rio Rancho, New Mexico
Posts: 4,583
Thanks: 958
Thanked 970 Times in 276 Posts
|
The Post War P.38 have a pretty high gloss black finish on them, though the slides are matt parkerized. The frames are aluminum. I dont know if they used anodizing or not.
__________________
Thor's Luger Clinic http://members.rennlist.com/lugerman/ Ted Green (Thor Yaller Boots) 725 Western Hills Dr SE, Rio Rancho, NM 87124 915-526-8925 Email thor340@aol.com ----------------------------------- John3:3 Jesus answered and said to him, "Most assuredly, I say to you, unless one is born again, he cannot see the kingdom of God." |
05-03-2012, 09:03 PM | #16 |
Twice a Lifer
Lifetime Forum Patron Join Date: Mar 2011
Location: Atop the highest hill in Schuyler County NY
Posts: 3,282
Thanks: 7,007
Thanked 2,476 Times in 1,319 Posts
|
alanint,
I found a couple links so far about home anodizing. Looks like fun! And this might be the culprit--as far as finishing pot metal guns. it fits all the criteria: It can be any color. It offers corrosion and abrasion resistance (up to Rockwell 70!). It can be rubbed out for increased gloss. And any dimension it adds, typically up to 4 mils, dimension to the parts in a controllable way. Interesting...I already have some expendable parts for practice/testing, and most of the equipment and chemicals; just need to pick up some black and dark blue Rit dyes. What do you think? http://www.warpig.com/paintball/technical/anodize.shtml http://www.defelsko.com/applications.../Anodizing.htm DP |
The following member says Thank You to ithacaartist for your post: |
05-04-2012, 04:02 AM | #17 |
User
Join Date: May 2004
Posts: 1,538
Thanks: 18
Thanked 36 Times in 21 Posts
|
Anodizing does indeed look like fun. Wonder how it would work on steel..
Btw. I thought all Lugers where painted like this
__________________
Previously known as Morgan Kane |
05-04-2012, 08:59 PM | #18 |
Patron
LugerForum Patron Join Date: Feb 2012
Location: Southern Indiana
Posts: 237
Thanks: 1,238
Thanked 126 Times in 84 Posts
|
Urrppp!
"Btw. I thought all Lugers where painted like this..."
I just threw up in my mouth a little. I will never, ever, make fun of my "Krome Kannon" again! |
05-04-2012, 09:41 PM | #19 | |
Twice a Lifer
Lifetime Forum Patron Join Date: Mar 2011
Location: Atop the highest hill in Schuyler County NY
Posts: 3,282
Thanks: 7,007
Thanked 2,476 Times in 1,319 Posts
|
Quote:
The aspects of anodizing similar to galvanizing--which is a very hot dip in molten zinc--are the layer formed between the outside skin of the treatment and the original material beneath, and the phenomenon of slight dimensional growth of a part so treated. This layer is like an alloy because the molecules of the base metal and those of the coating are intermingled. Curiously, the growth is accelerated in the galvanizing process in areas of the treated material with higher silica content. So, if you'd welded a joint with regular alloy steel filler and ground and sanded the joint smooth and flush, it will look as if someone had taken a caulking gun to the weld after it emerges from the dip tank. DP |
|
05-05-2012, 03:17 AM | #20 |
User
Join Date: May 2004
Posts: 1,538
Thanks: 18
Thanked 36 Times in 21 Posts
|
GySgt1811; It's indeed repulsive. I'm ashamed to admit that I'm the Bubba who desecrated it
Don't forget to post some pictures of the result if you go ahead with anodizing those parts David
__________________
Previously known as Morgan Kane |
|
|