Lead filled Luger

ithacaartist · 02-03-2024, 06:00 PM

Happy Saturday, everyone,

A friend of my buddy Steve--who runs Gunblack in Interlaken NY-- has dropped off a couple of Lugers for him to restore. One is a matching Mauser Banner, but the one in question is a matching 1938 Military Mauser.

It was plated (I think nickel) without a lot of obnoxious buffing. The big question is what to best do about how it was "deactivated." The end of the barrel and the action were poured full of melted lead. The toggle knobs are raised around a half inch above their intended position in battery, and everything is frozen/locked in this position. Therefore, exact extent and location of what Pb was poured into the action is unknown.

Since the temp needed to melt the lead is below that which would affect any of the gun's heat treating, I've tentatively advised that the grips be removed and the gun set up and heated so that as much lead as possible will melt and run out, perhaps helped along by compressed air.

The melting process will not remove it all, of course, but enough needs to go that would allow the upper, TD lever, etc to move enough again for its disassembly. I'm thinking that donning a pair of good, heavy oven mitts might allow moving the related parts while they're still hot enough, before the residual lead has re-solidified.

Does anyone have experience performing this trick, or suggestions about another approach? (I am remiss in that I came away without snapping at least one pic, sorry.)

gunbugs · 02-03-2024, 06:41 PM

That is a good plan. Wear an apron, and some goggles, along with your welding gloves, and "get hot". I've removed seriously stuck bullets, sometimes several stacked up, using heat.

Edward Tinker · 02-03-2024, 07:18 PM

In one of the vet bring backs, two 1911a1's were brought back to the USA by this method. They were taken down into parts, then put in the base of a lamp and lead filled around them.
Shipped home
Once home, they simply heated the base up and cleaned up the guns.
I imagine it wasn't as easy as the story told, but the two guns were used for years afterwards I wa told.

Ed

ithacaartist · 02-04-2024, 01:59 PM

Quote:

Originally Posted by Edward Tinker

In one of the vet bring backs, two 1911a1's were brought back to the USA by this method. They were taken down into parts, then put in the base of a lamp and lead filled around them.
Shipped home
Once home, they simply heated the base up and cleaned up the guns.
I imagine it wasn't as easy as the story told, but the two guns were used for years afterwards I wa told.

Ed

Very clever! ...Although they probably didn't wind up with any bring back paperwork this way!

Kiwi · 02-04-2024, 11:40 AM

Use your oven method to control heat, forget the compressed air, but go for 2-3 trips to the oven.
Like a blacksmith working iron, heat pour off what lead you can, return to heat.

G.T. · 02-04-2024, 12:35 PM

Hi David, I would do all of the above, Then!!! I would first give it a few soaks and cleans in a commercial bore cleaner / lead remover? Or find out what the active ingreadient (NOT ACID) is and soak it in that, Then!!!! I would set up a chem 10 electrolisis (sp.?) tank and make the part an anode (or cathode? Not sure about direction, (wax on, wax off

!) which would get every last molocule of lead... It would take some research, but i think basically easy once you get into it... Best, til.....lat'r.....GT

02-03-2024, 06:00 PM	#1
ithacaartist Twice a Lifer Lifetime Forum Patron Join Date: Mar 2011 Location: Atop the highest hill in Schuyler County NY Posts: 3,346 Thanks: 7,275 Thanked 2,578 Times in 1,365 Posts	Lead filled Luger Happy Saturday, everyone, A friend of my buddy Steve--who runs Gunblack in Interlaken NY-- has dropped off a couple of Lugers for him to restore. One is a matching Mauser Banner, but the one in question is a matching 1938 Military Mauser. It was plated (I think nickel) without a lot of obnoxious buffing. The big question is what to best do about how it was "deactivated." The end of the barrel and the action were poured full of melted lead. The toggle knobs are raised around a half inch above their intended position in battery, and everything is frozen/locked in this position. Therefore, exact extent and location of what Pb was poured into the action is unknown. Since the temp needed to melt the lead is below that which would affect any of the gun's heat treating, I've tentatively advised that the grips be removed and the gun set up and heated so that as much lead as possible will melt and run out, perhaps helped along by compressed air. The melting process will not remove it all, of course, but enough needs to go that would allow the upper, TD lever, etc to move enough again for its disassembly. I'm thinking that donning a pair of good, heavy oven mitts might allow moving the related parts while they're still hot enough, before the residual lead has re-solidified. Does anyone have experience performing this trick, or suggestions about another approach? (I am remiss in that I came away without snapping at least one pic, sorry.) __________________ "... Liberty is the seed and soil, the air and light, the dew and rain of progress, love and joy."-- Robert Greene Ingersoll 1894

02-03-2024, 07:18 PM	#3
Edward Tinker Super Moderator Eternal Lifer LugerForum Patron Join Date: Jun 2002 Location: North of Spokane, WA Posts: 15,933 Thanks: 2,032 Thanked 4,530 Times in 2,092 Posts	In one of the vet bring backs, two 1911a1's were brought back to the USA by this method. They were taken down into parts, then put in the base of a lamp and lead filled around them. Shipped home Once home, they simply heated the base up and cleaned up the guns. I imagine it wasn't as easy as the story told, but the two guns were used for years afterwards I wa told. Ed __________________ Edward Tinker ************ Co-Author of Police Lugers - Co-Author of Simson Lugers Author of Veteran Bring Backs Vol I, Vol II, Vol III and Vol IV

02-04-2024, 12:35 PM	#6
G.T. Lifer Lifetime Forum Patron Join Date: Jun 2002 Location: Chandler Arizona Posts: 3,507 Thanks: 1,318 Thanked 3,653 Times in 1,004 Posts	I would! Hi David, I would do all of the above, Then!!! I would first give it a few soaks and cleans in a commercial bore cleaner / lead remover? Or find out what the active ingreadient (NOT ACID) is and soak it in that, Then!!!! I would set up a chem 10 electrolisis (sp.?) tank and make the part an anode (or cathode? Not sure about direction, (wax on, wax off !) which would get every last molocule of lead... It would take some research, but i think basically easy once you get into it... Best, til.....lat'r.....GT

02-03-2024, 06:41 PM	#2
gunbugs Lifetime Forum Patron Join Date: Sep 2013 Location: Fairbanks, Alaska. Home of the best moose. Posts: 658 Thanks: 365 Thanked 1,176 Times in 393 Posts	That is a good plan. Wear an apron, and some goggles, along with your welding gloves, and "get hot". I've removed seriously stuck bullets, sometimes several stacked up, using heat.

02-04-2024, 11:40 AM	#5
Kiwi User Join Date: Mar 2019 Location: Wrong side of the Delaware river Posts: 307 Thanks: 215 Thanked 435 Times in 172 Posts	Use your oven method to control heat, forget the compressed air, but go for 2-3 trips to the oven. Like a blacksmith working iron, heat pour off what lead you can, return to heat.