It looks like a production error, which would not be unheard of in the German's haste to turn pistols out in 1943. I say this because there are no stress marks, cracks or folds, which would surely be evident if someone had tried to bend this after the initial cooling, hardening had taken place. If may have been overheated during production then was overly bent during machining.
|